LLDPE, LLDPE Film, HDPE manufacturer / supplier in China, offering Linear Low Density Polyethylene LLDPE, Sinopec 1500 High Lipolytic PP Resin for Melt-Blown Nonwoven Fabric, PP Resin (MFI; 1500) for Making Melt Blow Woven and so on.

Gold Member Since 2013
Audited Supplier

Linear Low Density Polyethylene LLDPE

Min. Order / Reference FOB Price
18 Tons US $1,250/ Ton
Port: Tianjin, China
Production Capacity: 5000mt Per Month
Payment Terms: L/C, T/T, D/P, Western Union
CAS No.: 13463-67-7
Formula: LLDPE
EINECS: 20170612
Material: Linear Low Density Polyethylene/LLDPE
Usage: General Plastics, Engineering Plastics, Specialty Plastics
Plastic Properties After Heated: Thermoplastic Plastics

You Might Also Like

Loading...

Basic Info.

Model NO.
LLDPE
Plastic Forming Method
Blow Molding
Color
White
Place of Origin
Hebi China
Quanlity
Virgin
Service
OEM/ODM
Trademark
sino
Transport Package
25/50kg Per Plastic Bag, About 20TM Per FCL
Specification
sgs, iso9001, ce
Origin
China
HS Code
3901100001
1, LLDPE film grade
 

Tests

Value

Unit

Melt Flow Rate (MFR)

2.0±0.4

g/10min

Density

920±2

Kg/cm3

Tensile Strengthat Yield

8

Mpa ≥

Tensile Strengthat Break

12

Mpa ≥

haze

15

%≤

Packing

In 25 kg PP woven bags,20MT/20'FCL




2, LLDPE for Master Batch Use

Tests

Value

Unit

Melt Flow Rate (MFR)

20

g/10min

Density

0.924

g/cm3

Tensile Strength

MD12

Mpa

TD 10

Elongation at Yield

13

%

Elongation at Break

200

Dark Drop Impact

105

g

Brittle Temperature(F 50)

-70

°C

Vicat Softening Point

90

°C

Packing

In 25 kg PP woven bags,20MT/20'FCL




3, LLDPE Powder Rotational Molding Grade for Tank Use

Tests

Value

Unit

Melt Flow Rate (MFR)

3.2

g/10min

Density

0.939

g/cm3

Melting Point

127

°C

Tensile Yield Strength

21

Mpa

Tensile Strength at Break

28

Mpa

Elongation at Break

1,100

%

Flexural Modulus

750

Mpa

Brittle Temperature

<-60

°C




Tests Value Unit
Melt Flow Rate (MFR) 2.0± 0.4 g/10min
Density 920± 2 Kg/cm3
Tensile Strengthat Yield 8 Mpa ≥
Tensile Strengthat Break 12 Mpa ≥
Haze 15 %≤
Packing In 25 kg PP woven bags, 20MT/20'FCL

2, LLDPE Powder Rotational Molding Grade for Tank Use
Tests Value Unit
Melt Flow Rate (MFR) 3.2 g/10min
Density 0.939 g/cm3
Melting Point 127 ° C
Tensile Yield Strengt 21 Mpa
Tensile Strength at Break 28 Mpa
Elongation at Brea 1, 100 %
Flexural Modulus 750 Mpa
Brittle Temperature <-60 ° C

Application
1 Fiber (Carpet, Textiles, Upholstery, etc. )
2 Film (Shopping bags, casting film, multilayer film, etc. )
3 Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
4 Extrusion Molding (Sheet, Pipe, Wire & Cable, etc. )
5 Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc. )...

Send your message to this supplier

*From:
*To:
avatar Mr. Xin Li
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Loading...

Product Categories

Contact Supplier