General Purpose Polystyrene GPPS

• Customization: Available
• CAS No.: 13463-67-7
• Formula: 305768499/458
• Model NO.: GPPS
• EINECS: 20170612
• Material: Polyphenylenesulfide/PPS
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Lamination
• Color: Oyster White
• Place of Origin: Shandong China (Mainland)
• Model Number: Virgin /Recycle
• Service: OEM/ODM
• Transport Package: 25/50kg Per Plastic Bag, About 20TM Per FCL
• Specification: SGS
• Trademark: sinopec
• Origin: China Mainland
• HS Code: 3903199000
• Production Capacity: 10, 000.00reams Per Month

Product Description

GPPS: General Purpose Polystyrene

Physical and Chemical Properties
Appearance : Clear pellets
Solubility in water: Insoluble
Density: 1.04-1.111 g/cm3 (20 C)
Usage: Common commercial polymer.



Introduction of GPPS:
General Purpose Polystyrene is a kind of thermoplastic resin, is a colorless, odorless, tasteless, shiny, transparent beaded or granular solid. Density is 1.04 to 1.09, transparency is 88% to 92%, refractive index is 1.59 to 1.60. In the stress function, resulting in birefringence, the so-called stress - optical effect. Product of the melting temperature is 150 to 180 ° C, thermal decomposition temperature is 300 ° C, the heat distortion temperature is 70 to 100 ° C, long-term use temperature is 60 ~ 80 °C
 
Specification of GPPS Resin:
Data-1

Item	Test conditions	Test method	Test data	unit
Density		ISO 1183:1987	1040	kg/m3
Water absorption		ISO 62:1999	<0.1	%
Melt flow rate	200°C/5kg	ISO 1133:1997	3.8	cm3/10min
Process shrinkage		ISO 294-4:1997	0.4-0.6	%
Charpy impact strength	1eU	ISO 179:1993	15	kj/m2
Tensile modulus	1mm/min	ISO 527-2:1993	3300	MPa
Elongation	50mm/min	ISO 527-2:1993	3	%
Tensile strength at break	50mm/min	ISO 527-2:1993	55	MPa
Ball indentation hardness H	358N/30s	ISO 2039-1:1993	150	N/mm2
Bending strength	2mm/min	ISO 178:1993	100	MPa
HDT	1.8MPa	ISO 75-2:1993	84	°C
Linear coefficient of thermal expansion	(23-80)°C	DIN 53 752	0.8-1.0	K-1
Heat conduction		DIN 52 612	0.16	W/mK
Vicat softening point	B50/oil	ISO 306:1994	93	°C

 
Data-2

Item	Testing standards	Test Conditions	Units	PG-22	PG-33	PG-80	PG-80N
Melt flow index	D-1238	200°C*5kg	g/10min.	17.5	7.4	4.0	5.7
Softening point	D-1525	1kg.	°C	87.0	94.0	97.7	97.6
Tensile strength	D-638		Kg/cm²	420	470	500	490
Tensile modulus	D-638	-		26460	26220	26720	26720
Bending strength	D-790	-	Kg/cm²	540	670	690	690
Flexural modulus	D-790		Kg/cm²	31000	31000	31000	31000
Heat distortion temperature	D-648	-	°C	75	79	81	81
Use	-	-	-	Mixed leveling	Injection level	Injection level	Injection level

 
 Handling and Storage:
[Storage]
Store in a tightly closed container. Store in a cool, dry, well-ventilated area away from incompatible substances.
[Handling]
Wash thoroughly after handling. Remove contaminated clothing and wash before reuse. Use with adequate ventilation. Minimize dust generation and accumulation. Avoid contact with eyes, skin, and clothing. Keep container tightly closed. Avoid ingestion and 
 
1 Packing: 25kg/pp bag, 25kg/paper bag, 1000kg/jumbo bag, 500kg/super sack
2 Loading: 17mt per 20 foot container
3 Loading Port: Any China Port
4 Lead time: 20days